Corrosion, a white putty like substance - which is eating away at the aluminium, is showing on a couple of domestic windows. Nobody, builder or supplier, wants to accept responsibilty. Any ideas - what the cause(s) might be and/or how to rectify the problem. Or even how to have a go at the builder and/or supplier.
Thanks,
Bob H.
Ask a large Al supplier if they have heard of the problem.
Ask the Aus Al Council or whatever theyre called - I asked them some questions recently, very helpful.
After that you may have something to pin down whoever is liable
Good luck
Quote:
Originally Posted by hawkinob
The metal, Aluminium, is actually quite reactive and very easily oxidised.Quote:
Originally Posted by hawkinob
So what you actually "see" when you look at things made from aluminium is the coating of aluminium oxide. Scrape it - and the metal almost instantaneously re-oxidises... Now Aluminium oxide is actually quite stable which is why 'aluminium' products last so long - without corroding...
I'd suggest that your piece of aluminium actally contains some impurity introduced at the smelter - and it's this 'impurity' that is corroding - not the aluminium...
But how you convince the supplier is a matter for a lawyer - maybe a metallurgist's report would help...
Jedo
How close to the ocean are you? Salt air will do quite a stunt on Al, unless anodized, and maybe even then depending on concentration.
Joe
I just googled "aluminium corrosion" - tons of refs
Like this:
http://www.alu-info.dk/HTML/alulib/modul/A00100.htm
As Joe Greiner said - salt (sodium chloride - NaCl) will attack Al2O3 but would be generalised - all over - whereas I gathered from yur post that it was "spot" damage...
Anyways - research it via google...
Are your windows anodised....
Jedo
Between 9 and 10 kilometres, nearer 10 I reckon.Quote:
Originally Posted by joe greiner
Bob H.
The supplier's letter says 'Powder coated' and they say:-Quote:
Originally Posted by Jedo_03
"we suspect that the underlying cause is a result of crevice corrosion...'.
Bob H.
p.s. I'll go to the website you mentioned. I'm really at a loss to understand how the builder and /or window supplier can deny responsibilty, it's just a domestic dwelling!!!!!!
How old are the windows?Quote:
Originally Posted by hawkinob
I wonder if it was initiated by an incompetent brick cleaner
Ten years BUT I first reported this to both the builder and the window supplier in 2001. At that time the supplier said 'brick cleaning', the builder said 'No, not brick cleaning', the supplier then offered a choice - scrape out and repair or replace the damaged section. Considered that a repair would suffice, on condition that it worked. It hasn't. Now the supplier has come up with 'crevice corrosion.Quote:
Originally Posted by Big Shed
Bob H.
Quote:
Originally Posted by echnidna
The damage, except for one window, is at floor level and where the mortar upright joints occur. The one window which is different has sings of corrosion at one jamb, again at mortar joints.
Bob H.
Anything more than 1 or 2 km from the ocean shouldn't be affected by salt air corrosion. More often seen on bridge railings directly above salt water. Sounds like the old game of "the other guy." Best consult a professional if the stakes are high enough.
Joe
It almost sounds like salt attack, does the brickwork have fluffy salt deposits on it?Quote:
Originally Posted by hawkinob
If so, then the mortar had salt in it.
Al :?
Thanks to all you responded. I live in hope of a resolution!!!!
Regards,